Microleakage in class II restorations of two bulk fll resin composites and a conventional nanohybrid resin composite: an in vitro study at 10,000 thermocycles
Ver/
Descargar
(application/pdf: 1.218Mb)
(application/pdf: 1.218Mb)
Fecha
2021-10-28Autor(es)
Cayo‑Rojas1, César Felix2
Hernández‑Caba2, Karen K
Aliaga‑Mariñas2, Ana S.
Ladera‑Castañeda1, Marysela I.2
Cervantes‑Ganoza3, Luis A
Metadatos
Mostrar el registro completo del ítemResumen
Background: The contraction presented by resin composites causes an increase in stress at the tooth-resin interface,
causing micro-gaps that allow microleakage. This study aims to evaluate the degree of in vitro marginal microleakage
in class II restorations with two bulk fll resin composites compared to a conventional nanohybrid resin composite.
Methods: The present study was an in vitro experimental design. A total of 30 standardized class II cavities were
prepared in 15 human molars (mesially and distally). These cavities were later distributed in 3 groups according to the
type of resin. Groups A and B were restored with bulk fll resin composites (Filtek—3 M/ESPE and Tetric N-Ceram—Ivo‑
clar/Vivadent respectively) in a single increment of 4 mm. Group C was restored with the Filtek Z350 XT – 3 M/ESPE
resin composite and two increments of 2 mm. Later, the restorations were subjected to 10,000 thermocycles between
5 °C to 55 °C and immersed in a silver nitrate solution (1 M for 24 h). The crowns were then sectioned mesiodistally
and observed under the stereomicroscope to determine the degree of marginal microleakage at the occlusal and
cervical areas. The results were analyzed with the Kruskal–Wallis and the Mann–Whitney U statistical tests.
Results: There were no statistically signifcant diferences regarding the degree of microleakage between the three
types of resin composites in the occlusal and cervical areas (p>0.05). Similarly, there were no signifcant diferences
after comparing each resin type in its occlusal and cervical area (p>0.05).
Conclusion: Filtek Bulk Fill and Tetric N-Ceram Bulk Fill resin composites showed no statistically signifcant diferences
with the conventional nanohybrid resin composite Filtek Z350XT at both occlusal and cervical areas.
Keywords: Monoblock resin, Composite resin, Marginal adaptation, Microleakage, Molar, Mono incremental resin,
Silver nitrate, Thermal cycling, Tooth preparation
Palabras clave
Colecciones
El ítem tiene asociados los siguientes ficheros de licencia:
Ítems relacionados
Mostrando ítems relacionados por Título, autor o palabras clave.
-
Surface Roughness in Nanoparticle Resin Composites Subjected to Two Polishing Systems: An In vitro Comparative Study
Cayo Rojas, César Félix; Ramírez-Vargas, Giovanna Gisella; Ladera-Castañeda, Marysela I.; López-Gurreonero, Carlos; Cornejo-Pinto, Alberto; Cachay-Criado, Hernán; Cervantes-Ganoza, Luis Adolfo (Journal of International Society of Preventive and Communitary Dentistry, 2022-11-11)Acceso abiertoAim: The surface roughness of dental restorations can decrease resin durability, since it leads to its deterioration, color variation, and loss of gloss. Therefore, the aim was to assess the surface roughness of ... -
Surface roughness and oxygen inhibited layer control in bulk‑fll and conventional nanohybrid resin composites with and without polishing: in vitro study
Gaviria‑Martinez, Andrea; Castro‑Ramirez, Leonor; Ladera‑Castañeda, Marysela; Cervantes‑Ganoza, Luis; Cachay‑Criado, Hernán; Alvino‑Vales, María; Garcia‑Luna, Goretty; López‑Gurreonero, Carlos; Cornejo‑Pinto, Alberto; Cayo‑Rojas, César F. (BMC Oral Health, 2022-06-26)Acceso abiertoBackground: It has been demonstrated that dental restorations with rough surfaces can have several disadvantages such as pigment retention or plaque accumulation, which can facilitate caries formation, color variation, ... -
Surface Microhardness of Bulk-Fill Resin Composites Handled With Gloves
Cayo Rojas, César Félix; Berto-Inga, Julissa; Santander-Rengifo, Flor; Ladera-Castaneda, Marysela; Lopez-Gurreonero, Carlos; Castro Pérez-Vargas, Antonieta; Cornejo-Pinto, Alberto; Cervantes-Ganoza, Luis (International Dental Journal (IDJ), 2022-11-17)Acceso abiertoAim: It has been reported that resin composites may experience alterations in their mechanical properties when they come into contact with glove powder. Therefore, the present study aimed to compare the surface microhardness ...